BS EN ISO 5832-3:2016 pdf free.Implants for surgery – Metallic materials Part 3: Wrought titanium 6-aluminium 4-vanadium alloy (ISO 5832-3:2016).
This part of Iso 5832 specifies the characteristics of, and corresponding test methods for, the wrought titanium alloy known as titanium 6-aluminium 4-vanadium alloy (Ti 6-AI4-V alloy) for use in the manufacture of surgical implants.
NOTE The mechanical properties of a sample obtained from a finished product made of this alloy may not necessarily comply with the specifications given in this part of ISO 5832.
2 Normative references
The following documents, in whole or in part, are normatively referenced in this document and are indispensable for its application. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies.
ISO 6892-1 1), Metallic materials — Tensile testing — Part 1: Method of test at room temperature Iso 7438, Metallic materials — Bend test
Iso 20160, Implants for surgery — Metallic materials — Classification of microstructures for alpha* beta titanium alloy bars
EN 3114-003, Aerospace series — Test method — Microstructure of (a÷fJ) titanium alloy wrought products — Part 003: Microstructure of plate
3 Terms and definitions
For the purposes of this document, the terms and definitions given in ISO 6892-1 and the following apply.
3.1 original gauge length L0 length between gauge length marks on the test piece measured at room temperature before the test ISOURCE: ISO 6892-1:—, 3.1.1)
4 Chemical composition
The heat/ingot analysis of a representative sample of the alloy when determined in accordance with
Clause 6 shall comply with the chemical composition specified in Table 1.
NOTE 1 Ingot analysis may be used for determining all chemical requirements except hydrogen. The analysis of hydrogen shall be carried out after the final heat treatment and final surface treatment.
5 Microstructure
The microstructure, when examined as indicated in Table 3, shall be alpha + beta globular and shall correspond to photomicrographs A1 to A9 in ISO 20160 for round bars or 3T1 to 3T13 in EN 3114-003 for sheet and plates (annealed condition each).
6 Mechanical properties
6.1 Tensil The tensile properties of the alloy, when tested in accordance with Clause Z shall comply with the values specified in Table 2.BS EN ISO 5832-3 pdf download.